PP compound 6614 is a mineral filled modified polypropylene. This material combines high flow, good impact and a high stiffness level with a low shrinkage and CLTE. Typical applications include automotive exterior parts such as large thin wall zero gap bumper designs but also lateral siding and bumper strips. It can be used in painted and unpainted applications with UV stabilization added on demand.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.00 | g/cm³ | ISO 1183 |
熔流率（熔体流动速率） (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
收缩率 1 (24小时, 3.20 mm) | 0.75 | % | 内部方法 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
肖氏硬度 (邵氏 D) | 60 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 1350 | MPa | ISO 527-2/1A |
拉伸应力 | ISO 527-2/1A | ||
屈服 | 19.0 | MPa | |
断裂 | 18.0 | MPa | |
拉伸应变 (断裂) | 500 | % | ISO 527-2/1A |
弯曲模量 2 | 1350 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 (23°C) | 35 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 (-40°C) | 40 | kJ/m² | ISO 179/1eU |
悬壁梁缺口冲击强度 | ISO 180/1A | ||
-20°C | 10 | kJ/m² | |
0°C | 无断裂 | ||
23°C | 无断裂 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 (0.45 MPa, 未退火) | 100 | °C | ISO 75-2/B |
维卡软化温度 | 130 | °C | ISO 306/A |